A study of hydrogen, oxygen and nitrogen bonding in a-Si thin films by IR spectroscopy
Talukder, G., Cornish, J.C.L., Jennings, P.J., Hefter, G.T., Lund, C.P., Clare, B.W. and Livingstone, J. (1992) A study of hydrogen, oxygen and nitrogen bonding in a-Si thin films by IR spectroscopy. In: Arden, M.E., Burley, S.M.A. and Coleman, M., (eds.) Solar World Congess: Proceedings of the Biennial Congress of the International Solar Energy Society, Denver, Colarado, 19-23 August 1991. Pergamon Press, Oxford, UK, pp. 15-20.
*Open access. Some pages may not be available
Fourier transform infrared (FTIR) spectroscopy has been used to study the nature of hydrogen, oxygen and nitrogen bonds In a-Si thin films. The samples were prepared by rf sputtering under different deposition conditions to produce hydrogen contents ranging from 15 to 35 at.%. Slightly contaminated samples were found to contain nitrogen and oxygen ranging from 0.0 - 1.5 and 0.0 - 3.0 at.% respectively. Annealing vas performed by heating the samples in a hydrogen atmosphere, usually for 30 minutes, at temperatures ranging from 150 to 550 C. The FTIR spectra, taken for the as-deposited sample and after each annealing step, have been deconvoluted into their component peaks using the simplex algorithm. Our results demonstrate that for a particular type of silicon-hydrogen group, evolution of hydrogen takes place at a lower temperature from the surface and/or the near surface region than from the bulk, On the other hand, oxygen and nitrogen related bonds in the a-Si network change configurations on annealing.
|Publication Type:||Book Chapter|
|Murdoch Affiliation:||School of Mathematical and Physical Sciences|
|Copyright:||© 1992 International Solar Energy Society|
|Item Control Page|